With the development of industry and the subsequent awareness of the adverse health effects from air pollution exposure, separation and treatment of organic pollutants in air has become an increasingly important aspect of air pollution control (1,2). At present, the use of air purifiers has become popular in removing air pollutants. Traditional air purifiers use filters or adsorption materials for this purpose (3,4). These methods just transfer the pollutants to another phase instead of removing them, and additional disposal steps are subsequently required (3). An alternative technique, which is a promising, effective and green technology for pollution control, is heterogeneous photocatalytic oxidation (PCO) (5-8). PCO actually oxidizes pollutants to H2O and O2 (1,2) and is cost-effective in comparison with other similar conventional technologies because semiconductors are inexpensive (9). The energy source of photocatalytic processes is natural/UV light; therefore, this method is low in energy consumption but highly effective in degrading most organic compounds (10). Different kinds of photocatalysts such as pure or doped metal oxides (e.g., TiO2+, CdS, ZnO, Fe(III)-doped TiO2) and chalcogenides have been developed (4,7,10).Among these, titanium dioxide has been the dominant photocatalyst because of its strong oxidizing power, especially for aromatic compounds, high photocorrosion resistance, and its nontoxic, stable and inexpensive characteristics, all of which facilitate removing harmful organic compounds in the air and water (8,11,12). However, TiO2photocatalyst alone has low efficiency due to its small specific surface area (2,8), and recombination of electron-hole pairs (9,13). In addition, its performance is not quite well under visible light (5). On the other hand, the link between the fine particle of TiO2 and the carrier cannot be fast enough and the carrier has a negative effect on photochemical catalyst (14). For these reasons, many efforts have been devoted to minimizing these restrictions and improving the performance of the dominant photocatalyst TiO2. In this regard, TiO2 nanoparticle has to be supported (immobilized) on noble metals (e.g., Au, Ag, Pt) nanoparticles, activated carbon and zeolite (e.g., Y, ZSM-5). However, both TiO2 and metal nanoparticles are unstable and tend to assemble in larger structures, which will reduce the photocatalystic performance (5). Instead, carbon structures can be used for the distribution of TiO2 particle and increased sensitivity to visible light as well as hindering the recombination of electron-hole pairs (5,10,14). Meanwhile, different literatures have reported enhanced photocatalytic activity of TiO2 supported on zeolites compared with bare TiO2(6,13,15).However, few, if any, studies have considered supporting TiO2 on activated carbon and zeolites in order to remove air pollutants. Given the above mentioned benefits of using TiO2 supported on activated carbon and zeolite in the photocatalytic process, the present work considered how effective this can be in removing gaseous styrene, as an important volatile organic compounds (VOCs) widely used in the production of synthetic rubber, resins, polyesters and plastics and a proven carcinogenic, mutagenic, and teratogenic agent (5,8,16). Therefore, the main purpose of this study was to determine the synergistic effect of nano-TiO2 immobilized on activated carbon, zeolite Y and ZSM-5 on the removal of styrene from air pollution.Zeolite Y and ZSM-5 were produced in China and purchased from Iran zeolite store. Activated carbon was obtained from Merk CO. These materials were used either as an adsorbent or as TiO2 support in this study with 20-40 mesh. Degussa Nano-TiO2-P25 was from purchased from Germany. Styrene (purity ? 99.98%) was obtained from Merck, Germany.2.2. Preparation of AC-TiO2? Y-TiO2 and ZSM-5-TiO2 catalystsIn this study, the weight percentage of TiO2 nanoparticles in the adsorbent coating was selected at 5 %. Many studies reported this to be an appropriate portion portion(17). For the preparation of AC-TiO2 catalyst, at first a specific mass of TiO2 was weighed by scale (precision 0.0001), then it was poured into the Arlon containing deionized water and stirred in an ultrasonic generator (Starsonic 18-35.Italy) for 30 min. In this stage, TiO2 nanoparticles were completely separated and this provided a homogenous suspension. After this stage, a specific amount of activated carbon was added on the suspension. 2.3. Characterization of AC-TiO2, Y-TiO2 and ZSM-5/TiO2 catalysts The AC-TiO2, Y-TiO2 and ZSM-5/TiO2 catalysts were characterizedfor surface morphology, specific surface area and X-ray diffraction. The surface morphology of the catalysts was analyzed using the Field Emission Scanning Electron Microscopy (FESEM) technique (Model of MIRA3TESCAN-XMU made, Manufacturing Corporation of TSCANAmerica). Evaluations for BET specific surface area of the catalysts was determined by QuantachromeChem BET Instrument. 2.4. Experimental set-up and analytical methodThe experimental set up in this study is shown in Fig 1. The system consisted of three sections. 1) Input section 2) Adsorb and removal section 3) Sampling system.Styrene was injected by a syringe pump (manufacturing Co Hitachi Ltd) in three different concentrations (20, 100 and 300 ppm in air). Styrenevapors were produced by bubbling method in which pure air was passed into a styrene generator (composed of a water bath and a wash bottle filled with styrene), and the produced styrene vapor was mixed with pure air as balance gas in the mixing chamber. Photocatalystremoval section was carried out in a photoreactor containing 2 gr of catalyst. The reactor designed for this study was a cylindrical reactor of quartz glass (to pass UV rays). Illumination was provided by an 8-W UVA lamp that was placed in the center of reactor and three 6-W UVA lamps that were located outside the reactor in a distance of 5 cm from the reactor. According to similar studies, it was found that nanoparticles of TiO2 and ZnO in the presence of UVA with wavelength of 356 nm have the highest photocatalytic function function(18). The length, internal diameter and thickness of this reactor were 280 mm, 20 mm and 2 mm respectively, and it had an inlet at the top and an outlet at the bottom in opposite directions.The sampling section consisted of a sampling port at the outlet and at the inlet of the reactor. A portable photoionization VOC detector (Phocheck Tiger, model of 5000, Ion Science Ltd., UK), with a detection limit of 1 ppb – 10,000 ppm, was used to detect the concentration of styrene. In order to ensure the measurement accuracy, some concentrations were also measured by GC (Philips PU4410) equipped with FID detector and Phochek Tiger.Finally the performance index of the catalysts was calculated using adsorption capacity and removal efficiency as follows relations (19):where BC is the mass of styrene fed to the adsorber divided by mass of adsorbent at the breakthrough, mg/g; Q is the air flow rate to adsorber, m3/h; C is the concentration of styrene, mg/m3; tbk is the breakthrough time (the time of being observed styrene in the exit gas stream), h; and Madsorbent is the mass of adsorbent, gr.3. ResultsCharacterization of the prepared catalystsThe crystal phase of the prepared AC-TiO2, Y-TiO2 and ZSM-5/TiO2 catalysts was analyzed by X-ray diffraction (XRD). X-ray diffraction analysis was performed to assay the phase composition and crystalline nature of the prepared catalysts. It is shown in Fig 2. We observed various diffraction peaks of TiO2 at 2?=25.3°, 27.57, 36.23, 37.8, 48.08°, 54.38°, 62.7°, given by AC-TiO2catalyst and diffraction peaks of TiO2 at 25.3°, and 48.08° by Y-TiO2 and ZSM-5/TiO2 catalysts. The BET specific surface areas and pore volumes of catalysts are summarized in Table 1. The specific surface areas of ZSM-5 zeolite, Y-zeolite and activated carbon decreased after loading TiO2 on them. The decrease of specific surface areas and pore volume and the average pore diameter of catalysts after loading TiO2 indicate that some TiO2 particles got into pore of catalysts and blocked some channels. The effect of various initial styrene concentrations (20, 100 and 300 ppm) on the photocatalytic removal efficiency of ZSM-5/TiO2, Y-TiO2 andAC-TiO2 catalysts were investigated and illustrated in Fig. 5. The result of photocatalytic degradation of styrene using AC-TiO2, Y-TiO2 and ZSM-5-TiO2 is shown in Fig 6. The difference of elimination of catalysts is due to the structure and specific surface area of catalysts and subsequently adsorption onto catalyst surface. The high catalytic activity of AC-TiO2 should be attributed to the interaction between AC and TiO2, which provides the appropriate ability to adsorb reactants by AC and catalytic oxidation of styrene by TiO2. Also the surface area of the AC is larger than Y-zeolite and ZSM-5-zeolite, causing more styrene molecules to be adsorbed and to be in contact with TiO2 and subsequently the photocatalytic removal efficiency of styrene is increased.Adsorption capacityThe adsorption capacity of the catalysts and adsorbents was investigated at different inlet concentrations (20, 100, and 300 ppm) and the results are presented The results show that, in all catalysts increasing the styrene concentration from 20 to 300 ppm decreases the removal efficiency. This finding is related to the kinetic effect and blocking the active sites. Increasing the concentration to 300 ppm makes the adsorption of more styrene molecules possible on the photocatalyst surface and these molecules will block more active sites on the catalyst surface and lead to a reduction of the hydroxyl radical generation on the photocatalyst surface. This phenomenon brings about the deactivation of the catalyst and reduces the production of active species on the photocatalyst surface leading to the decrease of photocatalytic removal efficiency of styrene at higher concentrations (22,23).Also at a low concentration, the adsorption rate of the pollutants over the surface of catalysts is obviously slower than the oxidation reaction rate. Therefore, the adsorption of the gas-phase pollutants is the major factor that determines the removal rate. As the concentration of the pollutants increase, the adsorption and reaction rate get closer, and both of these are important for the overall removal rate. When the concentrations of the pollutants increase to a high level (ppm), the adsorption is much quicker than the photooxidation, and the photoactivity should be the rate controlling factor.The results of this study showed that at each styrene concentration, the overall photodegradation catalyst efficiency varied as: AC-TiO2>Y-TiO2> ZSM-5/TiO2, respectively. In all adsorbents and adsorbents coated with TiO2, with increasing the inlet concentration of styrene, the breakthrough time decreases while the adsorption capacity increases. Studies show that of the higher the concentration, the more mass of pollutants per unit of time removed from air current, so the breakthrough time and saturation of adsorbent reduce (24,25). The results also demonstrated that the adsorption capacity and breakthrough of adsorbents coated with TiO2 was higher than those of bare adsorbents in all samples. Comparing the performance of bare adsorbents with that of coated adsorbents indicates that the latter could remove much more styrene from the waste air stream than the former under similar experimental conditions. One of the effective factors in adsorption capacity is the specific surface area of the material. In this study, the correlation between specific surface area of the adsorbent and the adsorption capacity of styrene showed the following relation in terms of adsorption capacity AC > Y-Zeolite> ZSM-5 Zeolite. Also the results indicated the high surface area and adsorption capacity of photocatalyst can exert a positive influence on their photocatalytic performance. The greater styrene adsorption capacity of coated adsorbents with TiO2 compared to bare adsorbents must play a role in the photoactivity of TiO2. Some researchers (26,27) have determined that with the presence of TiO2, the hydroxyl (OH°) concentration is increased and the degradation process takes a shorter time to complete. This can increase the breakthrough time. The results also demonstrated that photocatalysts with high adsorptive capacity enhanced the subsequent photocatalysis reactions and led to a positive synergistic effect.In conclusion, we have demonstrated that bare TiO2 had a low photocatalytic activity in removal of styrene, but by the loading of TiO2 on adsorbent (AC, Y and ZSM-5 zeolite) the photocatalytic performance enhances. Among catalysts, AC-TiO2 showed a much stronger photocatalytic degradation of styrene molecules than did Y-TiO2 and ZSM-5/TiO2. Factors like the high surface area of AC and the interaction between AC and TiO2 may cause enhanced photocatalytic activity of AC-TiO2. According to our result and those of other studies, high adsorption capacity and excellent mass transfer properties of these catalysts make these materials ideal candidates for industrial applications.